Harris® D620F1 Brazing Alloy, 0.05 x 0.125 in Dia, 20 in L

Description

Harris® Brazing Alloy, 1 lb Container, Stick Tube Container, 0.05 x 0.125 in Diameter, 20 in Length, 1300 to 1500 deg F, Composition: 6% Silver, 6.1% Phosphorous, 87.9% Copper

Dynaflow melts and flows at temperatures very close to Stay Silv 15, and provides comparable brazed mechanical properties. This makes Dynaflow an excellent cost effective alternative to the 15% silver alloys. This premium, medium range silver alloy has been meticulously formulated to even tighter specifications than our standard copper-to-copper alloys.

Features

• Premium, medium-range alloy for brazing copper or brass.
• Excellent strength and ductility
• Economical replacement of 15% silver alloys
• When heated quickly to its liquidus, allows penetration into tight clearance connections
• Wide melting range provides ability to fill loose connections and "cap" or "build up" around the finished joint
• Self-fluxing on copper and copper-to-copper connections. Use STAY-SILVv® white flux for brazing brass or copper-to brass
• Not recommended for brazing steel or other ferrous base metals
• Corrosion resistance is generally similar to the copper base metal, but phosphorus containing alloys, including DYNAFLOW®, should not be used if the braze is exposed to sulfur or sulfur compounds in service
• Phosphorus content promotes formation of low ductility intermetallic with the base metal
• Conforms to the EU Reach & RoHS directive